交叉轧制周期对高纯Ta板变形及再结晶梯度的影响
祝佳林1,刘施峰1(
),曹宇1,柳亚辉1,邓超1,2,刘庆1,2
),曹宇1,柳亚辉1,邓超1,2,刘庆1,2
Effect of Cross Rolling Cycle on the Deformed and Recrystallized Gradient in High-Purity Tantalum Plate
Jialin ZHU1,Shifeng LIU1(),Yu CAO1,Yahui LIU1,Chao DENG1,2,Qing LIU1,2
),Yu CAO1,Yahui LIU1,Chao DENG1,2,Qing LIU1,2
图6. 1和2周期Ta板表面与中心层晶粒在1050 ℃退火不同时间的OIMs
Fig.6. OIMs of 1 and 2 cycle samples annealed at 1050 ℃ for 5 min (a1~d1), 10 min (a2~d2), 30 min (a3~d3), 60 min (a4~d4) and 120 min (a5~d5)Color online(a1~a5) 1 cycle, surface (b1~b5) 1 cycle, center(c1~c5) 2 cycles, surface (d1~d5) 2 cycles, center