阳极氧化法制备Zr-17Nb合金表面氧化物纳米管阵列及其性能研究
李玲1,姚生莲1,赵晓丽2,3,杨佳佳1,王野熹1,王鲁宁1,4(
)
)
Fabrication and Properties of Anodic Oxide Nanotubular Arrays on Zr-17Nb Alloy
Ling LI1,Shenglian YAO1,Xiaoli ZHAO2,3,Jiajia YANG1,Yexi WANG1,Luning WANG1,4()
)
图8. Zr-17Nb合金、阳极氧化120 min及阳极氧化120 min并经过450 ℃退火处理制备的纳米管阵列的表面接触角
Fig.8. Surface contact angles of Zr-17Nb alloy (a), nanotubular arrays prepared by anodic oxidation for 2 h before (b) and after (c) annealing at 450 ℃