阳极氧化法制备Zr-17Nb合金表面氧化物纳米管阵列及其性能研究
|
李玲 1,姚生莲 1,赵晓丽 2,3,杨佳佳 1,王野熹 1,王鲁宁 1,4( )
|
Fabrication and Properties of Anodic Oxide Nanotubular Arrays on Zr-17Nb Alloy
|
Ling LI 1,Shenglian YAO 1,Xiaoli ZHAO 2,3,Jiajia YANG 1,Yexi WANG 1,Luning WANG 1,4( )
|
|
图7. Zr-17Nb合金、阳极氧化120 min及阳极氧化120 min并经过450 ℃退火处理制备的纳米管阵列的XPS
|
Fig.7. XPS survey spectra of three groups of samples (Zr-17Nb, nanotubular array prepared by anodizing for 120 min, nanotubular array prepared by anodizing for 120 min and annealing at 450 ℃) (a) and high resolution spectra of Zr3d (b), Nb3d (c), O1s (d) and F1s (e) on nanotubular array anodized for 120 min before and after annealing treatment at 450 ℃ |
|
|
|
|