阳极氧化法制备Zr-17Nb合金表面氧化物纳米管阵列及其性能研究
|
李玲 1,姚生莲 1,赵晓丽 2,3,杨佳佳 1,王野熹 1,王鲁宁 1,4( )
|
Fabrication and Properties of Anodic Oxide Nanotubular Arrays on Zr-17Nb Alloy
|
Ling LI 1,Shenglian YAO 1,Xiaoli ZHAO 2,3,Jiajia YANG 1,Yexi WANG 1,Luning WANG 1,4( )
|
|
图1. 阳极氧化制备纳米管过程中电流密度随时间变化关系图和阳极氧化最初2 min内电流密度随时间变化关系图
|
Fig.1. Variation of current density with anodic oxidation duration (Inset shows current density transition during the first 2 min of anodization: I—the portion where current density rapidly decreases; II—the portion where current density slowly increases; III—the portion where current density slowly decreases) |
|
|
|
|