GH984G合金在700 ℃水蒸气中的氧化行为
王常帅1(
),郭莉莉1,唐丽英2,周荣灿2,郭建亭1,周兰章1
),郭莉莉1,唐丽英2,周荣灿2,郭建亭1,周兰章1
Oxidation Behavior of GH984G Alloy in Steam at 700 ℃
Changshuai WANG1(),Lili GUO1,Liying TANG2,Rongcan ZHOU2,Jianting GUO1,Lanzhang ZHOU1
),Lili GUO1,Liying TANG2,Rongcan ZHOU2,Jianting GUO1,Lanzhang ZHOU1
图3. GH984G合金在700 ℃蒸汽条件下氧化不同时间后表面形貌的SEM像
Fig.3. Low (a, c, e, g, i) and high (b, d, f, h, j) magnified surface SEM images of scales formed on GH984G alloy oxidized at 700 ℃ for 100 h (a, b), 300 h (c, d), 500 h (e, f), 1000 h (g, h) and 2000 h (i, j)