地质处置低氧过渡期X65低碳钢腐蚀行为研究
刘灿帅1,2,田朝晖2,张志明1,王俭秋1(
),韩恩厚1
),韩恩厚1
Corrosion Behaivour of X65 Low Carbon Steel During Redox State Transition Process of High LevelNuclear Waste Disposal
Canshuai LIU1,2,Zhaohui TIAN2,Zhiming ZHANG1,Jianqiu WANG1(),En-Hou HAN1
),En-Hou HAN1
图12. X65低碳钢在80 ℃低氧饱和膨润土中的平均腐蚀速率随时间变化的拟合结果
Fig.12. Fitting results of the relationship between average corrosion rate (V) and time when X65 low carbon steel has been immersed in saturated bentonite at 80 ℃ (R2—variances between three parallel tests)