Corrosion Behaivour of X65 Low Carbon Steel During Redox State Transition Process of High LevelNuclear Waste Disposal
Canshuai LIU1,2,Zhaohui TIAN2,Zhiming ZHANG1,Jianqiu WANG1(),En-Hou HAN1
),En-Hou HAN1
图11. X65低碳钢在80 ℃低氧饱和膨润土中浸泡150 d后腐蚀产物截面区域(图9d中方框区域)的元素分布
Fig.11. Elemental distributions on cross section (selected area in Fig.9d) of corrosion products formed on X65 low carbon steel immersed in saturated bentonite at 80 ℃ for 150 d