地质处置低氧过渡期X65低碳钢腐蚀行为研究
刘灿帅1,2,田朝晖2,张志明1,王俭秋1(
),韩恩厚1
),韩恩厚1
Corrosion Behaivour of X65 Low Carbon Steel During Redox State Transition Process of High LevelNuclear Waste Disposal
Canshuai LIU1,2,Zhaohui TIAN2,Zhiming ZHANG1,Jianqiu WANG1(),En-Hou HAN1
),En-Hou HAN1
图10. X65低碳钢在80 ℃低氧饱和膨润土中浸泡150 d后的腐蚀产物典型微观形貌
Fig.10. Typical micro morphologies including blocks (a), slices (b), rods (c) and swellings (d) of corrosion products on X65 low carbon steel in saturated bentonite at 80 ℃ for 150 d