地质处置低氧过渡期X65低碳钢腐蚀行为研究
刘灿帅1,2,田朝晖2,张志明1,王俭秋1(),韩恩厚1
Corrosion Behaivour of X65 Low Carbon Steel During Redox State Transition Process of High LevelNuclear Waste Disposal
Canshuai LIU1,2,Zhaohui TIAN2,Zhiming ZHANG1,Jianqiu WANG1(),En-Hou HAN1

图9. X65低碳钢在80 ℃低氧饱和膨润土中腐蚀不同时间后的截面形貌

Fig.9. Cross sectional morphologies of X65 low carbon steel immersed in anoxic saturated bentonite at 80 ℃ for 10 d (a), 50 d (b), 100 d (c) and 150 d (d)