Mo元素及热处理对Ni2CrFeMox高熵合金在NaCl溶液中耐蚀性能的影响
魏琳1,王志军1(
),吴庆峰1,尚旭亮2,李俊杰1,王锦程1
),吴庆峰1,尚旭亮2,李俊杰1,王锦程1
Effect of Mo Element and Heat Treatment on Corrosion Resistance of Ni2CrFeMox High-Entropy Alloyin NaCl Solution
Lin WEI1,Zhijun WANG1(),Qingfeng WU1,Xuliang SHANG2,Junjie LI1,Jincheng WANG1
),Qingfeng WU1,Xuliang SHANG2,Junjie LI1,Jincheng WANG1
图8. 铸态和热处理态Ni2CrFeMo0.2合金在3.5%NaCl溶液中恒电位+450 mV极化4 h后的XPS谱
Fig.8. XPS spectra of as-cast (a1~a4) and heat-treated (b1~b4) Ni2CrFeMo0.2 alloy in 3.5%NaCl solution after constant potential+450 mV (vs SHE) polarization for 4 h