Mo元素及热处理对Ni2CrFeMox高熵合金在NaCl溶液中耐蚀性能的影响
魏琳1,王志军1(
),吴庆峰1,尚旭亮2,李俊杰1,王锦程1
),吴庆峰1,尚旭亮2,李俊杰1,王锦程1
Effect of Mo Element and Heat Treatment on Corrosion Resistance of Ni2CrFeMox High-Entropy Alloyin NaCl Solution
Lin WEI1,Zhijun WANG1(),Qingfeng WU1,Xuliang SHANG2,Junjie LI1,Jincheng WANG1
),Qingfeng WU1,Xuliang SHANG2,Junjie LI1,Jincheng WANG1
图2. 铸态Ni2CrFeMox合金和316L不锈钢在3.5%NaCl溶液中极化后的SEM像
Fig.2. SEM images of the as-cast Ni2CrFeMox alloys with x=0.1 (a), x=0.2 (b), x=0.3 (c), x=0.4 (d), x=0.5 (e) and 316L stainless steel (f) polarized in 3.5%NaCl solution