α+β两相钛合金元素再分配行为及其对显微组织和力学性能的影响
黄森森1,2,马英杰1(
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
Influence of Alloying Elements Partitioning Behaviors on the Microstructure and Mechanical Propertiesin α+β Titanium Alloy
Sensen HUANG1,2,Yingjie MA1(),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
图3. 不同两相区温度固溶后水冷条件下，TC4合金αp及βt的元素(Al、V)定量分析
Fig.3. Quantitative measurements of element concentrations in αp and βt with respect to solution temperature in α+β phase region followed by water quenching