α+β两相钛合金元素再分配行为及其对显微组织和力学性能的影响
黄森森1,2,马英杰1(
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
Influence of Alloying Elements Partitioning Behaviors on the Microstructure and Mechanical Propertiesin α+β Titanium Alloy
Sensen HUANG1,2,Yingjie MA1(),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
图11. 两相区固溶后空冷条件下，TC4合金βt的纳米压痕性能随固溶温度的变化
Fig.11. Variations of E and H of βt in the samples with solution and A.C. condition as a function of solution temperature