α+β两相钛合金元素再分配行为及其对显微组织和力学性能的影响
黄森森1,2,马英杰1(
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
Influence of Alloying Elements Partitioning Behaviors on the Microstructure and Mechanical Propertiesin α+β Titanium Alloy
Sensen HUANG1,2,Yingjie MA1(),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
图10. 原始态TC4合金中αp的纳米压痕性能随晶体取向的变化
Fig.10. Variations of elastic modulus (E) and hardness (H) of αp in the as-received TC4 sample detected by nanoindentation