α+β两相钛合金元素再分配行为及其对显微组织和力学性能的影响
黄森森1,2,马英杰1(
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
Influence of Alloying Elements Partitioning Behaviors on the Microstructure and Mechanical Propertiesin α+β Titanium Alloy
Sensen HUANG1,2,Yingjie MA1(),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
图9. TC4合金经不同温度固溶空冷后βt区域内αs片层显微组织
Fig.9. Microstructures of αs lamella in βt of the TC4 samples soluted at different temperatures and followed by A.C.