α+β两相钛合金元素再分配行为及其对显微组织和力学性能的影响
黄森森1,2,马英杰1(
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
),张仕林1,齐敏1,雷家峰1,宗亚平2,杨锐1
Influence of Alloying Elements Partitioning Behaviors on the Microstructure and Mechanical Propertiesin α+β Titanium Alloy
Sensen HUANG1,2,Yingjie MA1(),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
),Shilin ZHANG1,Min QI1,Jiafeng LEI1,Yaping ZONG2,Rui YANG1
图4. TC4合金经880 ℃固溶并以不同方式冷却后的显微组织及Al、V元素浓度分布
Fig.4. Microstructures and corresponding element concentration distributions of the TC4 samples soluted at 880 ℃ and followed by different cooling conditions (The color scale represents element concentration, with red referring to high, while blue low contents)