B含量对K417G合金凝固过程中组织演变和力学性能的影响
刘巧沐1,黄顺洲1,刘芳2,杨艳3,南宏强3,张东3,孙文儒2(
)
)
Effect of Boron Content on Microstructure Evolution During Solidification and Mechanical Properties of K417G Alloy
Qiaomu LIU1,Shunzhou HUANG1,Fang LIU2,Yan YANG3,Hongqiang NAN3,Dong ZHANG3,Wenru SUN2()
)
图1. 不同B含量K417G合金铸态组织的OM像
Fig.1. OM images of the as cast K417G alloy with 0.0017%B (a), 0.0059%B (b), 0.012%B (c) and 0.060%B (d)