E690高强低合金钢焊接热影响区典型组织在含SO2海洋环境中的应力腐蚀行为对比研究
马宏驰1,2,杜翠薇1,刘智勇1(
),李永1,李晓刚1,3
),李永1,李晓刚1,3
Comparative Study of Stress Corrosion Cracking Behaviors of Typical Microstructures of Weld Heat-Affected Zones of E690 High-Strength Low-Alloy Steel in SO2-Containing Marine Environment
Hongchi MA1,2,Cuiwei DU1,Zhiyong LIU1(),Yong LI1,Xiaogang LI1,3
),Yong LI1,Xiaogang LI1,3
图10. 图8b插图中ICHAZ组织周浸10 d除锈后表面凸起部分的EDS分析
Fig.10. EDS analysis of marked area in the inset of Fig.8b of simulated ICHAZ after 10 d corrosion test