固溶温度对Mn-N型双相不锈钢拉伸变形行为的影响
金淼1,李文权1,郝硕1,2,梅瑞雪1,李娜1,陈雷1,2(
)
)
Effect of Solution Temperature on Tensile Deformation Behavior of Mn-N Bearing Duplex Stainless Steel
Miao JIN1,Wenquan LI1,Shuo HAO1,2,Ruixue MEI1,Na LI1,Lei CHEN1,2()
)
图5. 1200 ℃固溶后Mn-N合金化双相不锈钢变形30%的组织EBSD分析
Fig.5. EBSD analysis of deformed microstructure (30%) of the Mn-N bearing DSSs specimen solution treated at 1200 ℃ (A, B, C indicate martensites of different nucleation and growth mode, the microstructures inside the circles are slip bands or (and) deformation bands. GB—grain boundary)