固溶温度对Mn-N型双相不锈钢拉伸变形行为的影响
金淼1,李文权1,郝硕1,2,梅瑞雪1,李娜1,陈雷1,2(
)
)
Effect of Solution Temperature on Tensile Deformation Behavior of Mn-N Bearing Duplex Stainless Steel
Miao JIN1,Wenquan LI1,Shuo HAO1,2,Ruixue MEI1,Na LI1,Lei CHEN1,2()
)
图4. 不同固溶温度下Mn-N合金化双相不锈钢样品EBSD与带对比度分析
Fig.4. EBSD (a, c) and band contrast (b, d) analyses of microstructures near the fracture surface of Mn-N bearing DSSs specimen solution treated at the temperatures of 1050 ℃ (a, b) and 1200 ℃ (c, d) (The microstructures inside the circles are slip bands or (and) deformation bands)