焊接线能量对5182-O/HC260YD+Z异种材料CMT搭接接头组织与性能的影响
吉华1,2,邓运来3(
),徐红勇2,郭伟强2,邓建峰2,范世通3
),徐红勇2,郭伟强2,邓建峰2,范世通3
The Influence of Welding Line Energy on the Microstructure and Property of CMT Overlap Joint of 5182-Oand HC260YD+Z
Hua JI1,2,Yunlai DENG3(),Hongyong XU2,Weiqiang GUO2,Jianfeng DENG2,Shitong FAN3
),Hongyong XU2,Weiqiang GUO2,Jianfeng DENG2,Shitong FAN3
图13. 典型试样断口形貌
Fig.13. Typical fracture morphologies of samples S3 (a~c) and S5 (d~f)(a) "fusion interface" fracture (b) SEM image of middle area (c) partial magnification of area in Fig.13b (d) "brazing interface" fracture (e, f) partial magnifications of area in Fig.13d