The Influence of Welding Line Energy on the Microstructure and Property of CMT Overlap Joint of 5182-Oand HC260YD+Z
Hua JI1,2,Yunlai DENG3(),Hongyong XU2,Weiqiang GUO2,Jianfeng DENG2,Shitong FAN3
),Hongyong XU2,Weiqiang GUO2,Jianfeng DENG2,Shitong FAN3
图5. 钎焊界面形成过程示意图
Fig.5. Schematics of the brazing interface formation showing liquid molten pool (a), primary γ-Fe phase, γ-Fe+FeAl mixed phase precipitation (b), fine columnar crystal FeAl precipitation (c), planar FeAl2 precipitation (d) and atypical columnar crystal FeAl3 precipitation (e)