Sn对锆合金在280 ℃ LiOH水溶液中初期腐蚀行为的影响
姚美意1,2(
),林雨晨1,2,侯可可1,2,梁雪1,2,胡鹏飞1,2,张金龙1,2,周邦新1,2
),林雨晨1,2,侯可可1,2,梁雪1,2,胡鹏飞1,2,张金龙1,2,周邦新1,2
Effect of Sn on Initial Corrosion Behavior of Zirconium Alloy in 280 ℃ LiOH Aqueous Solution
YAO Meiyi1,2(),LIN Yuchen1,2,HOU Keke1,2,LIANG Xue1,2,HU Pengfei1,2,ZHANG Jinlong1,2,ZHOU Bangxin1,2
),LIN Yuchen1,2,HOU Keke1,2,LIANG Xue1,2,HU Pengfei1,2,ZHANG Jinlong1,2,ZHOU Bangxin1,2
图7. 2种合金小晶粒样品和2种合金大晶粒样品在不同条件水溶液中的腐蚀增重曲线
Fig.7. Corrosion gain curves of two alloys with fine grains in 360 ℃, 18.6 MPa and 0.01 mol/L LiOH aqueous solution (a), and of two alloys with large grains in 280 ℃, 6.3 MPa and 0.01 mol/L aqueous solution (b)