Sn对锆合金在280 ℃ LiOH水溶液中初期腐蚀行为的影响
姚美意1,2(
),林雨晨1,2,侯可可1,2,梁雪1,2,胡鹏飞1,2,张金龙1,2,周邦新1,2
),林雨晨1,2,侯可可1,2,梁雪1,2,胡鹏飞1,2,张金龙1,2,周邦新1,2
Effect of Sn on Initial Corrosion Behavior of Zirconium Alloy in 280 ℃ LiOH Aqueous Solution
YAO Meiyi1,2(),LIN Yuchen1,2,HOU Keke1,2,LIANG Xue1,2,HU Pengfei1,2,ZHANG Jinlong1,2,ZHOU Bangxin1,2
),LIN Yuchen1,2,HOU Keke1,2,LIANG Xue1,2,HU Pengfei1,2,ZHANG Jinlong1,2,ZHOU Bangxin1,2
图1. 1#合金(Zr-0.75Sn-0.35Fe-0.15Cr)大晶粒TEM薄样品在280 ℃、6.3 MPa、0.01 mol/L LiOH水溶液中短时腐蚀后的TEM像和SAED花样
Fig.1. TEM images (a~f) and corresponding SAED patterns (a1~f1) of 1# alloy (Zr-0.75Sn-0.35Fe-0.15Cr) large-grain TEM thin sample after short-time corrosion in 280 ℃, 6.3 MPa and 0.01 mol/L LiOH aqueous solution (Figs.1a~f are taken every 500 nm from thick to thin along the diameter of the hole)