粉末高温合金中SiO2夹杂物与基体的界面反应机理及对其变形行为的影响
冯业飞,周晓明,邹金文(
),王超渊,田高峰,宋晓俊,曾维虎
),王超渊,田高峰,宋晓俊,曾维虎
Interface Reaction Mechanism Between SiO2 and Matrix and Its Effect on the Deformation Behavior of Inclusionsin Powder Metallurgy Superalloy
FENG Yefei,ZHOU Xiaoming,ZOU Jinwen(),WANG Chaoyuan,TIAN Gaofeng,SONG Xiaojun,ZENG Weihu
),WANG Chaoyuan,TIAN Gaofeng,SONG Xiaojun,ZENG Weihu
图1. 名义尺寸为30 和60 μm的植入SiO2粉末颗粒的SEM像和EDS
Fig.1. SEM images and EDS (insets) of implanted SiO2 powder particles with the nominal dimensions of 30 μm (a) and 60 μm (b)