Re和Ta对抗热腐蚀单晶高温合金900 ℃长期时效组织稳定性的影响
黄太文1,卢晶1,许瑶1,王栋2,张健2,张家晨1,张军1,刘林1(
)
)
Effects of Rhenium and Tantalum on Microstructural Stability of Hot-Corrosion Resistant Single Crystal Superalloys Aged at 900 ℃
HUANG Taiwen1,LU Jing1,XU Yao1,WANG Dong2,ZHANG Jian2,ZHANG Jiachen1,ZHANG Jun1,LIU Lin1()
)
图6. 5Ta2Re和8Ta2Re合金经不同时间时效后析出的TCP相面积分数
Fig.6. Area fraction of TCP precipitates of 5Ta2Re and 8Ta2Re alloys after LTTE for different time