Re和Ta对抗热腐蚀单晶高温合金900 ℃长期时效组织稳定性的影响
黄太文1,卢晶1,许瑶1,王栋2,张健2,张家晨1,张军1,刘林1(
)
)
Effects of Rhenium and Tantalum on Microstructural Stability of Hot-Corrosion Resistant Single Crystal Superalloys Aged at 900 ℃
HUANG Taiwen1,LU Jing1,XU Yao1,WANG Dong2,ZHANG Jian2,ZHANG Jiachen1,ZHANG Jun1,LIU Lin1()
)
图3. 5种合金各组元在γ和γ′两相的分配系数(kiγ/γ′)
Fig.3. Partition ratios of alloying elements between γ and γ′ phases (kiγ/γ′) of the five alloys