节约型双相不锈钢TRIP效应致塑性增量及其固溶温度依赖性
陈雷1,2,郝硕1,2,梅瑞雪2,贾伟2,李文权2,郭宝峰2(
)
)
Intrinsic Increment of Plasticity Induced by TRIP and Its Dependence on the Annealing Temperature in a Lean Duplex Stainless Steel
CHEN Lei1,2,HAO Shuo 1,2,MEI Ruixue 2,JIA Wei 2,LI Wenquan 2,GUO Baofeng2()
)
图4. 典型固溶温度下LDX经不同温度拉伸后的工程应力-工程应变曲线
Fig.4. Engineering stress-engineering strain curves of the LDX after tension at different temperatures under typical annealing temperatures of 1000 ℃ (a), 1100 ℃ (b) and 1200 ℃ (c)