节约型双相不锈钢TRIP效应致塑性增量及其固溶温度依赖性
陈雷1,2,郝硕1,2,梅瑞雪2,贾伟2,李文权2,郭宝峰2()
Intrinsic Increment of Plasticity Induced by TRIP and Its Dependence on the Annealing Temperature in a Lean Duplex Stainless Steel
CHEN Lei1,2,HAO Shuo 1,2,MEI Ruixue 2,JIA Wei 2,LI Wenquan 2,GUO Baofeng2()

图3. LDX拉伸断口附近微观组织的TEM像

Fig.3. TEM images of microstructural features near the tensile fracture of the LDX(a) bright field image of austenite (b) dark field image of austenite and SAED patterns (insets) (c) bright field image of ferrite