中国低活化马氏体钢在液态Pb-Bi中的脆化现象
杨旭,廖波,刘坚,严伟,单以银,肖福仁,杨柯

Embrittlement Phenomenon of China Low Activation Martensitic Steel in Liquid Pb-Bi
Xu YANG,Bo LIAO,Jian LIU,Wei YAN,Yiyin SHAN,Furen XIAO,Ke YANG
图3 CLAM钢在200~500 ℃、Ar气和Pb-Bi共晶中拉伸速率为0.015 mm/min时的拉伸曲线
Fig.3 Tensile curves of CLAM steel in Ar and LBE under tensile strain rate of 0.015 mm/min at 200 ℃ (a), 250 ℃ (b), 450 ℃ (c) and 500 ℃ (d)