晶界特征对316不锈钢沿晶应力腐蚀开裂裂纹萌生的影响*
张子龙,夏爽(
),曹伟,李慧,周邦新,白琴
),曹伟,李慧,周邦新,白琴
EFFECTS OF GRAIN BOUNDARY CHARACTER ON INTERGRANULAR STRESS CORROSION CRACKING INITIATION IN 316 STAINLESS STEEL
Zilong ZHANG,Shuang XIA(),Wei CAO,Hui LI,Bangxin ZHOU,Qin BAI
),Wei CAO,Hui LI,Bangxin ZHOU,Qin BAI
图9. 经SCC 实验不同时间后316SS 中萌生裂纹的低SCSL晶界与晶界两侧晶粒Dm类别的关系
Fig 9. Dependence of fraction of cracked low SCSL grain boundaries on the Dm categories in 316SS after SCC test for different times