C对一种镍基高温合金与陶瓷型壳界面反应及润湿性的影响*
陈晓燕1,金喆2,白雪峰2,周亦胄1(
),金涛1,孙晓峰1
),金涛1,孙晓峰1
EFFECT OF C ON THE INTERFACIAL REACTION AND WETTABILITY BETWEEN A Ni-BASED SUPERALLOY AND CERAMIC MOULD
Xiaoyan CHEN1,Zhe JIN2,Xuefeng BAI2,Yizhou ZHOU1(),Tao JIN1,Xiaofeng SUN1
),Tao JIN1,Xiaofeng SUN1
图4. 合金(0.2%C)/陶瓷接触区附近陶瓷表面形貌及元素面分布
Fig.4. Microstructures around the alloy melt (0.2%C)/ceramic interaction area (a), detailed microstructure for areas I (b) and II (c) in Fig.4a, EPMA elemental distributions around the alloy melt (0.2%C)/ceramic interaction area (d1~d4)