长期时效对GH4169合金组织演化及低周疲劳行为的影响*
|
安金岚 1,王磊 1( ),刘杨 1,胥国华 2,赵光普 2
|
INFLUENCES OF LONG-TERM AGING ON MICRO- STRUCTURE EVOLUTION AND LOW CYCLE FATIGUE BEHAVIOR OF GH4169 ALLOY
|
Jinlan AN 1,Lei WANG 1( ),Yang LIU 1,Guohua XU 2,Guangpu ZHAO 2
|
|
图9. GH4169合金在750 ℃时效2000 h后低周疲劳断口附近横截面形貌
|
Fig.9. Morphologies of cross-section near LCF fracture surface in GH4169 alloy aged at 750 ℃ for 2000 h (The arrows indicate that the cracks propagate along the needle-like d phases) |
|
|
|
|