EFFECT OF LONG-TERM AGING AT 760 ℃ ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A Ni-Cr-W-Fe ALLOY
Xianchao HAO,Long ZHANG,Chao XIONG,Yingche MA(),Kui LIU
图4. 经760 ℃长期时效后Ni-Cr-W-Fe 合金中g’相形貌与分布
Fig.4. Morphologies and distributions of g’ phase in Ni-Cr-W-Fe alloy after aging at 760 ℃ for 200 h (a), 500 h (b), 1000 h (c), 2000 h (d) and 3000 h (e)