强磁场下不同晶粒尺寸Fe薄膜生长模式演变及其对磁性能的影响*
杜娇娇,李国建(
),王强,马永会,王慧敏,李萌萌
),王强,马永会,王慧敏,李萌萌
GROWTH MODE EVOLUTION AND SUBSEQUENT MAGNETIC PROPERTIES OF Fe FILMS WITH DIFFERENT GRAIN SIZES UNDER A HIGH MAGNETIC FIELD
Jiaojiao DU,Guojian LI(),Qiang WANG,Yonghui MA,Huimin WANG,Mengmeng LI
),Qiang WANG,Yonghui MA,Huimin WANG,Mengmeng LI
图3. 不同条件下制备的Fe薄膜的截面TEM像
Fig.3. Cross sectional TEM images of Fe films fabricated under different conditions (The width of columns was shown in Figs.3a2, b2, c2, d2 and f2. The diameter of grains was presented in Fig.3e2)
(a1, a2) 1350 ℃/0 T (b1, b2) 1350 ℃/6 T (c1, c2) 1400 ℃/0 T
(d1, d2) 1400 ℃/6 T (e1, e2) 1440 ℃/0 T (f1, f2) 1440 ℃/6 T