强磁场下不同晶粒尺寸Fe薄膜生长模式演变及其对磁性能的影响*
杜娇娇,李国建(
),王强,马永会,王慧敏,李萌萌
),王强,马永会,王慧敏,李萌萌
GROWTH MODE EVOLUTION AND SUBSEQUENT MAGNETIC PROPERTIES OF Fe FILMS WITH DIFFERENT GRAIN SIZES UNDER A HIGH MAGNETIC FIELD
Jiaojiao DU,Guojian LI(),Qiang WANG,Yonghui MA,Huimin WANG,Mengmeng LI
),Qiang WANG,Yonghui MA,Huimin WANG,Mengmeng LI
图6. 不同条件Fe薄膜的室温M-H曲线
Fig.6. Magnetic hysteresis (M-H) loops measured at room temperature by applying the magnetic fields perpendicular (a) and parallel (b) to the surface of Fe films under different conditions (M—magnetization, Ms—saturation magnetization, H// —applied field parallel to the film plane, H⊥—applied field perpendicular to the film plane)