取向硅钢中 114 418 织构对二次再结晶时晶粒异常长大的影响*
刘志桥,杨平(
),毛卫民,崔凤娥
),毛卫民,崔凤娥
EFFECT OF 114 418 TEXTURE ON ABNORMAL GROWTH DURING SECONDARY RECRYSTALLI- ZATION IN GRAIN-ORIENTED STEEL
Zhiqiao LIU,Ping YANG(),Weimin MAO,Feng'e CUI
),Weimin MAO,Feng'e CUI
图4. 高温退火时未渗氮样品在不同温度下的EBSD取向成像图
Fig.4. EBSD orientation images of samples at different temperatures during secondary recrystallization annealing
(a~f) orientation distribution maps of samples at 950, 975, 1025, 1050, 1075 and 1100 ℃, respectively
(g~l) ODF, φ2=45° at 950, 975, 1025, 1050, 1075 and 1100 ℃, respectively