X65钢在含超临界CO2的NaCl溶液中腐蚀机制的讨论*
魏亮,庞晓露,高克玮(
)
)
CORROSION MECHANISM DISCUSSION OF X65 STEEL IN NaCl SOLUTION SATURATED WITH SUPERCRITICAL CO2
Liang WEI,Xiaolu PANG,Kewei GAO()
)
图9. X65钢在9.5 MPa和80 ℃条件下在NaCl溶液中浸泡12 h形成的腐蚀产物膜的XRD谱
Fig.9. XRD spectrum of corrosion product scale on X65 steel immersed in NaCl solution for 12 h at 9.5 MPa and 80 ℃