X65钢在含超临界CO2的NaCl溶液中腐蚀机制的讨论*
魏亮,庞晓露,高克玮(
)
)
CORROSION MECHANISM DISCUSSION OF X65 STEEL IN NaCl SOLUTION SATURATED WITH SUPERCRITICAL CO2
Liang WEI,Xiaolu PANG,Kewei GAO()
)
图7. X65钢在含有饱和SC CO2的NaCl水溶液中浸泡不同时间后的腐蚀产物膜的表面形貌
Fig.7. Surface morphologies of corrosion product scale on X65 steel immersed in NaCl solution saturated with SC CO2 at 9.5 MPa and 80 ℃ for 12 h (a), 24 h (b), 50 h (c) and 168 h (d)