X65钢在含超临界CO2的NaCl溶液中腐蚀机制的讨论*
魏亮,庞晓露,高克玮(
)
)
CORROSION MECHANISM DISCUSSION OF X65 STEEL IN NaCl SOLUTION SATURATED WITH SUPERCRITICAL CO2
Liang WEI,Xiaolu PANG,Kewei GAO()
)
图5. X65钢在含水SC CO2相中浸泡96 h后形成的腐蚀产物膜的表面和截面形貌
Fig.5. Surface (a) and cross-section (b) morphologies of corrosion product scale on X65 steel in water-saturated SC CO2 phase after 96 h immersion