X65钢在含超临界CO2的NaCl溶液中腐蚀机制的讨论*
魏亮,庞晓露,高克玮(
)
)
CORROSION MECHANISM DISCUSSION OF X65 STEEL IN NaCl SOLUTION SATURATED WITH SUPERCRITICAL CO2
Liang WEI,Xiaolu PANG,Kewei GAO()
)
图13. X65钢在9.5 MPa 和80 ℃条件下浸泡在含有饱和SC CO2的NaCl水溶液和去离子水[9]中的腐蚀速率随浸泡时间的变化关系
Fig.13. Changes of corrosion rate of X65 steel in NaCl solution and deionized water[9] saturated with SC CO2 for various immersion time at 9.5 MPa and 80 ℃