X65钢在含超临界CO2的NaCl溶液中腐蚀机制的讨论*
魏亮,庞晓露,高克玮(
)
)
CORROSION MECHANISM DISCUSSION OF X65 STEEL IN NaCl SOLUTION SATURATED WITH SUPERCRITICAL CO2
Liang WEI,Xiaolu PANG,Kewei GAO()
)
图12. X65钢浸泡不同时间去膜后基体表面的粗糙度随浸泡时间的变化关系以及在0.5和96 h测得的基体表面轮廓图
Fig.12. Changes of roughness Ra of X65 matrix with immersion time after scale-removing (a) and the outline plots of X65 steel after 0.5 and 96 h immersions (b)