GH3535合金在FLiNaK熔盐中的腐蚀行为
刘涛1,2,董加胜2(
),谢光2,王义胜3,李辉2,李志军4,周兴泰4,楼琅洪2
),谢光2,王义胜3,李辉2,李志军4,周兴泰4,楼琅洪2
CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT
Tao LIU1,2,Jiasheng DONG2(),Guang XIE2,Yisheng WANG3,Hui LI2,Zhijun LI4,Xingtai ZHOU4,Langhong LOU2
),Guang XIE2,Yisheng WANG3,Hui LI2,Zhijun LI4,Xingtai ZHOU4,Langhong LOU2
图5. 带Al2O3涂层GH3535合金样品横截面腐蚀形貌的SEM像
Fig.5. Cross-sectional SE-SEM (a) and BSE-SEM (b) images of the GH3535 specimens with Al2O3 film immersed in FLiNaK molten salt at 700 ℃ for 400 h