GH3535合金在FLiNaK熔盐中的腐蚀行为
刘涛1,2,董加胜2(
),谢光2,王义胜3,李辉2,李志军4,周兴泰4,楼琅洪2
),谢光2,王义胜3,李辉2,李志军4,周兴泰4,楼琅洪2
CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT
Tao LIU1,2,Jiasheng DONG2(),Guang XIE2,Yisheng WANG3,Hui LI2,Zhijun LI4,Xingtai ZHOU4,Langhong LOU2
),Guang XIE2,Yisheng WANG3,Hui LI2,Zhijun LI4,Xingtai ZHOU4,Langhong LOU2
图 4. 无Al2O3涂层GH3535合金样品腐蚀后元素分布
Fig.4. Element distributions of the GH3535 specimen without Al2O3 film immersed in FLiNaK molten salt at 700 ℃ for 400 h
(a) Cr (b) Mo (c) Fe (d) O (e) Al (f) Ni