GH3535合金在FLiNaK熔盐中的腐蚀行为
刘涛1,2,董加胜2(
),谢光2,王义胜3,李辉2,李志军4,周兴泰4,楼琅洪2
),谢光2,王义胜3,李辉2,李志军4,周兴泰4,楼琅洪2
CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT
Tao LIU1,2,Jiasheng DONG2(),Guang XIE2,Yisheng WANG3,Hui LI2,Zhijun LI4,Xingtai ZHOU4,Langhong LOU2
),Guang XIE2,Yisheng WANG3,Hui LI2,Zhijun LI4,Xingtai ZHOU4,Langhong LOU2
图 3. 无Al2O3涂层GH3535合金样品熔盐腐蚀后横截面腐蚀形貌的SEM像
Fig.3. Cross-sectional SE-SEM (a) and BSE-SEM (b) images of the GH3535 specimens without Al2O3 film in FLiNaK molten salt at 700 ℃ for 400 h