SiCf/TC17复合材料拉伸行为研究
张旭,王玉敏(
),杨青,雷家峰,杨锐
),杨青,雷家峰,杨锐
STUDY ON TENSILE BEHAVIOR OF SiCf/TC17 COMPOSITES
Xu ZHANG,Yumin WANG(),Qing YANG,Jiafeng LEI,Rui YANG
),Qing YANG,Jiafeng LEI,Rui YANG
图6. SiCf/TC17复合材料室温拉伸断口中平坦区域的纵剖面典型形貌
Fig.6. Typical morphologies of longitudinal section related to the flat fracture regions in fracture surface of the SiCf/TC17 composites at room temperature
(a) partial macromorphology of longitudinal section
(b) multiple fracture of reaction layer near damaged fiber
(c) matrix cracking from the damaged reaction layer following fiber fracture
(d) flat fracture surface of matrix