Inconel 625熔敷金属中δ相的形核与粗化机理* |
||||||||||||
| 邸新杰, 邢希学, 王宝森 | ||||||||||||
|
NUCLEATION AND COARSENING MECHANISM OF δ PHASE IN INCONEL 625 DEPOSITED METAL |
||||||||||||
| DI Xinjie, XING Xixue, WANG Baosen | ||||||||||||
| 表1 不同保温时间下δ相的平均尺寸 | ||||||||||||
| Table 1 The average sizes of δ phase at different holding times | ||||||||||||
|
||||||||||||