电工钢柱状晶热、冷轧时晶界作用分析
邵媛媛, 杨平, 毛卫民
ANALYSIS ON GRAIN BOUNDARY EFFECTS OF COLUMNAR GRAINED ELECTRICAL STEEL
SHAO Yuanyuan, YANG Ping, MAO Weimin
表1
含3.5%Si电工钢单晶冷轧时的形状变化
[
20
]
Orientation
Rolling force / MPa
Average widening / %
Average extension / %
{100}<011>
<1
<2
101
{112}<110>
About 1
6
90
{111}<110>
About 5
10
84
{111}<112>
About 5
14
62