PITTING CORROSION DYNAMICS AND MECHANISMS OF 304 STAINLESS STEEL IN 3.5%NaCl SOLUTION |
DU Nan, TIAN Wenming, ZHAO Qing, CHEN Sibing |
National Defence Key Discipline Laboratory of Light Alloy Processing Science and Technology Institute, Nanchang Hangkong University, Nanchang 330063 |
|
Cite this article:
DU Nan TIAN Wenming ZHAO Qing CHEN Sibing. PITTING CORROSION DYNAMICS AND MECHANISMS OF 304 STAINLESS STEEL IN 3.5%NaCl SOLUTION. Acta Metall Sin, 2012, 48(7): 807-814.
|
Abstract Pitting rate of a single pit and pitting mechanisms of the 304 stainless steel in 3.5%NaCl solution were investigated by utilizing electronic speckle pattern interferometer (ESPI), electrochemical noise (EN) and three-dimensional video microscope. The results show that under 0.05 V polarization, the pitting corrosion process can be divided into four stages: drastic fluctuations of the current noise occured at 740 s, which means the passivation film was breaking, thus it can be concluded that the span of pitting incubation period is 740 s; a speckle occurred on the ESPI image at 750 s, thus the span of initiation period of the steady pitting is about 10 s; the growth rate of the pit increased during 750-780 s, which indicates that the pit corrosion is in active dissolution period; since then, the growth rate of the pit declined rapidly which means the pit was repassivated. After\linebreak 793 s, the growth rate of the pit raised again as secondary pits emerged. The pit image was observed and its volume was measured by three-dimensional video microscope, and the results were in agreement with those which were obtained by corrosion product concentration analysis. Some secondary pits were found in the bottom of the pit in three-dimensional reconstruction images.
|
Received: 04 January 2012
|
[1] Liao J X, Jiang Y M,WuWW, Zhong C, Li J. Acta Metall Sin, 2006; 42: 1187(廖家兴, 蒋益明, 吴玮巍, 钟澄, 李劲. 金属学报, 2006; 42: 1187)[2] Han D, Jiang Y M, Deng B, Zhang L H, Zhang W, Li J. Acta Metall Sin, 2009; 45: 919(韩冬, 蒋益明, 邓博, 张丽华, 张伟, 李 劲. 金属学报, 2009; 45: 919)[3] Dong C F, Luo H, Xiao K, Sun T, LiuQ, Li XG. J Wuhan Univ Technol–Mater Sci, 2011; 26: 641[4] Li H B, Jiang Z H, Yang Y, Cao Y, Zhang Z R. J Metall Mater, 2009; 16: 517[5] Li G M, Guo X P, Zheng J S. J Iron Steel Res, 2004; 11(4): 47[6] Hu L H, Du N, Wang M F, Zhao Q. J Chin Soc Corros Prot, 2007; 27: 233(胡丽华, 杜楠, 王梅丰, 赵晴. 中国腐蚀与防护学报, 2007; 27: 233)[7] Hong J F, Tan H, Chen L D, Li J, Li L, Jiang Y M. Acta Metall Sin, 2011; 47: 1445(洪巨峰, 谭华, 陈林豆, 李 劲, 李莉, 蒋益明. 金属学报, 2011; 47: 1445)[8] Tan Y J, Balley S, Kinsella B. Corros Sci, 1996; 38: 1681[9] Smulko J, Darouicki K. J Electroanal Chem, 2003; 545: 59[10] Wang M F, Du N, Li X G, Zhao Q, Liu G. Corros Prot, 2009; 30(1): 29(王梅丰, 杜楠, 李晓刚, 赵 晴, 刘 刚. 腐蚀与防护, 2009; 30(1): 29)[11] Wang M F, Li X G, Du N, Huang Y Z, Korsunsky A. Electrochem Commun, 2008; 10: 1000[12] Pan Y, Zhang S P, Zhou J L, Li X G, Xiao Y D. Equip Environ Eng, 2010; 7(4): 67(潘莹, 张三平, 周建龙, 李晓刚, 萧以德. 装备环境工程, 2010; 7(4): 67)[13] Lian C H, Gao Y. Chem Eng Mach, 1995; 22(2): 87(梁成浩, 高扬. 化工机械, 1995; 22(2): 87)[14] Ye T, Gao C Z. Mater Prot, 2007; 40(11): 78(叶涛, 高灿柱. 材料保护, 2007; 40(11): 78)[15] Liu G. Master Dissertation, Nanchang Hangkong Univ, 2008(刘刚. 南昌航空大学硕士学位论文, 2008)[16] Pujar M G, Anita T, Shaikh H, Dayul R K, Khatak H S. J Mater Eng Perform, 2007; 16: 494[17] Jong J K. Met Mater Int, 2011; 17: 777[18] Du N, Huang L, Xu S, Wang L Q. Failure Anal Prev, 2009; 4: 71(杜楠, 黄乐, 徐 珊, 王力强. 失效分析与预防, 2009; 4: 71)[19] Du N, Liu G, Zhao Q. Mater Sci, 2008; 2: 326[20] Jong J K. Met Mater Int, 2009; 15: 279[21] Girija S, Kamachi U, Mudali B R. Appl Electrochem, 2011; 41: 973[22] Yu Q B, Sun Y. Hot Work Technol, 2010; 39(2): 1(于庆波, 孙莹. 材料热处理技术, 2010; 39(2): 1)[23] Chen Y F, Rairdan R, Luo J L. Appl Electrochem, 1998; 28: 1371[24] Zhang J Q, Zhang Z. J Chin Soc Corros Prot, 2002; 22: 241(张鉴清, 张昭. 中国腐蚀与防护学报, 2002; 22: 241)[25] Zhang Z, Zhang J Q. Chin J Nonferrous Met, 2001; 11: 284(张昭, 张鉴清. 中国有色金属学报, 2001; 11: 284)[26] Li L, Li X G, Dong C f, Cheng Y F. Corros Eng Sci Tech, 2011; 46: 340[27] Sun D M, Jiang Y M, Tang Y, Xiang Q W, Zhong C, Liao J X, Li J. Electrochim Acta, 2009; 54: 1558[28] Frankel G S. J Electrochem Soc, 1998; 145: 2186 |
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|