模拟工业-海岸大气中SO2对Q235B钢腐蚀行为的影响*
陈文娟, 郝龙, 董俊华(), 柯伟, 文怀梁
中国科学院金属研究所金属腐蚀与防护国家重点实验室, 沈阳110016
EFFECT OF SO2 ON CORROSION EVOLUTION OF Q235B STEEL IN SIMULATED COASTAL- INDUSTRIAL ATMOSPHERE
CHEN Wenjuan, HAO Long, DONG Junhua(), KE Wei, WEN Huailiang
State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
引用本文:

陈文娟, 郝龙, 董俊华, 柯伟, 文怀梁. 模拟工业-海岸大气中SO2对Q235B钢腐蚀行为的影响*[J]. 金属学报, 2014, 50(7): 802-810.
Wenjuan CHEN, Long HAO, Junhua DONG, Wei KE, Huailiang WEN. EFFECT OF SO2 ON CORROSION EVOLUTION OF Q235B STEEL IN SIMULATED COASTAL- INDUSTRIAL ATMOSPHERE[J]. Acta Metall Sin, 2014, 50(7): 802-810.

全文: PDF(1251 KB)   HTML
关键词 Q235B钢干/湿交替工业-海岸大气腐蚀锈层    
Abstract

采用循环干/湿模拟腐蚀增重实验、动电位极化曲线、电化学阻抗谱和XRD方法, 研究了模拟海岸-工业大气中SO2对Q235B钢腐蚀行为的影响. 结果表明, 在腐蚀初期SO2抑制了Q235B钢的腐蚀; 在腐蚀后期, SO2促进了Q235B钢的腐蚀. 当SO2的浓度较低时, 腐蚀速率随SO2浓度的升高而增大; 当SO2的浓度较高时, 腐蚀速率随SO2浓度的升高而减小. 工业-海岸大气中的SO2组分可以抑制腐蚀产物中g -FeOOH和b -FeOOH的生成, 而促进a -FeOOH生成. 低碳钢腐蚀速率随SO2浓度变化出现的极值现象与SO2导致的锈层相组分变化密切相关.

Key wordsQ235B steel    dry/wet cyclic    coastal-industrial atmospheric corrosion    rust
收稿日期: 2013-11-15     
ZTFLH:  TG172.3  
基金资助:* 国家自然科学基金项目 51201170和 51131007资助
作者简介: null

陈文娟, 女, 1986年生, 博士生

图1  
图2  
Concentration / (mol·L-1) 1st stage 2nd stage 3rd stage 4th stage
0 1.220 0.820 - -
0.0010 1.183 0.942 - -
0.0017 1.200 0.978 - -
0.0050 1.067 0.869 - -
0.0300 1.165 0.798 - -
0.0900 0.885 1.578 1.017 0.858
  
图3  
图4  
图5  
图6  
图7  
图8  
[1] Leygraf C, Graedel T. Atmospheric Corrosion. New York: John Wiley & Sons, 2000: 10
[2] Singh D D N, Yadav S, Saha J K. Corros Sci, 2008; 50: 93
[3] Castaño J G, Botero C A, Restrepo A H, Agudelo E A, Correa E, Echeverría F. Corros Sci, 2010; 52: 216
[4] Hou W, Liang C. Corrosion, 1999; 55: 65
[5] Zhang Q C, Wu J S, Wang J J, Zheng W L, Li A B. Mater Chem Phys, 2002; 77: 603
[6] Mendoza A R, Corvo F. Corros Sci, 1999; 41: 75
[7] Dawson J L, Ferreira M G S. Corros Sci, 1986; 26: 1009
[8] Weissenrieder J, Leygraf C. J Electrochem Soc, 2004; 151: B165
[9] Hao L, Zhang S X, Dong J H, Ke W. Corros Sci, 2012; 58: 175
[10] Dong J H. Corros Sci Prot Technol, 2010; 22: 261
[10] (董俊华. 腐蚀科学与防护技术, 2010; 22: 261)
[11] Hao L, Zhang S X, Dong J H, Ke W. Metall Mater Trans, 2012; 43: 1724
[12] Wang J H, Wei F I, Chang Y S, Shih H C. Mater Chem Phys, 1997; 47: 1
[13] Misawa T, Hashimoto K, Shimodaira S. Corros Sci, 1974; 14: 131
[14] Evans U R, Taylor C A J. Corros Sci, 1972; 12: 227
[15] Saha J K. Corrosion of Constructional Steels in Marine and Industrial Environment. Heidelberg: Springer, 2013: 13
[16] Fuente D D L, Díaz I, Simancas J, Chico B, Morcillo M. Corros Sci, 2011; 53: 604
[17] Chen Y Y, Tzeng H J, Wei L I, Shih H C. Mater Sci Eng, 2005; A398: 47
[18] Ishikawa T, Katoh R, Yasukawa A, Kandori K, Nakayama T, Yuse F. Corros Sci, 2001; 43: 1727
[19] Asami K, Kikuchi M. Corros Sci, 2003; 45: 2671
[20] Shiotani K, Tanimoto W, Maeda C, Kawabata F, Amano K. Corros Eng, 2000; 49: 67
[21] Allam I M, Arlow J S, Saricimen H. Corros Sci, 1991; 32: 417
[22] Dong J H, Han E H, Ke W. Sci Technol Adv Mater, 2007; 8: 559
[23] Melchers R E. Corros Sci, 2008; 50: 3446
[24] Stramann M, Bohnenkamp K, Engell H J. Corros Sci, 1983; 23: 969
[25] Vaynman S, Guico R S, Fine M E, Manganello S J. Metall Mater Trans, 1997; 28A: 1274
[26] Mansfeld F. Corrosion, 1988; 44: 856
[27] Mansfeld F, Lin S, Chen Y C. J Electrochem Soc, 1988; 135: 906
[28] Stern M, Geary A L. J Electrochem Soc, 1957; 104: 56
[29] Revie R W, Uhlig H H. Corrosion and Corrosion Control. 4th Ed., New York: John Wiley & Sons, 2008: 115
[30] Stratmann M, Streckel H, Kim K T, Crockett S. Corros Sci, 1990; 30: 715
[31] Zhang S H, Lyon S B. Corros Sci, 1993; 35: 713
[32] Frankel G S, Stratmann M, Rohwerder M, Michalik A, Maier B, Dora J, Wicinski M. Corros Sci, 2007; 49: 2021
[1] 刘雨薇, 顾天真, 王振尧, 汪川, 曹公望. Q235Q450NQR1在中国南沙海洋大气环境中暴晒34个月后的腐蚀行为[J]. 金属学报, 2022, 58(12): 1623-1632.
[2] 李恺强, 杨璐嘉, 徐云泽, 王晓娜, 黄一. SO42-对模拟孔隙液中Q235B钢筋腐蚀行为的影响[J]. 金属学报, 2019, 55(4): 457-468.
[3] 卢云飞,董俊华,柯伟. SO42-对NiCu低合金钢在除氧NaHCO3溶液中腐蚀行为的影响[J]. 金属学报, 2015, 51(9): 1067-1076.
[4] 卢云飞, 阳靖峰, 董俊华, 柯伟. NiCu低合金钢在含Cl-的除氧NaHCO3溶液中的腐蚀行为研究[J]. 金属学报, 2015, 51(4): 440-448.
[5] 陈文娟, 郝龙, 董俊华, 柯伟, 文怀梁. 模拟工业-海岸大气中pH值对Q235B钢腐蚀行为的影响*[J]. 金属学报, 2015, 51(2): 191-200.
[6] 彭欣 王佳 山川 王海杰 刘在健 邹妍. 带锈碳钢在流动海水中的长期腐蚀行为[J]. 金属学报, 2012, 48(10): 1260-1266.
[7] 刘杰 李相波 王佳. 模拟深海压力对2种低合金钢腐蚀行为的影响[J]. 金属学报, 2011, 47(6): 697-705.
[8] 高新亮 朱苗勇 付贵勤 汪峰 邓志银. 桥梁耐候钢在含Cl-离子环境中的腐蚀行为[J]. 金属学报, 2011, 47(5): 520-527.
[9] 曹国良 李国明 陈珊 常万顺 陈学群. 海水飞溅区Ni-Cu-P钢的锈层和耐点蚀性能研究[J]. 金属学报, 2011, 47(2): 145-151.
[10] 曹国良 李国明 陈珊 常万顺 陈学群. 典型耐海水腐蚀钢中Ni和Cr耐点蚀作用的比较[J]. 金属学报, 2010, 46(6): 748-754.
[11] 柯伟 董俊华. Mn-Cu钢大气腐蚀锈层演化规律及其耐候性的研究[J]. 金属学报, 2010, 46(11): 1365-1378.
[12] 邹妍 郑莹莹 王燕华 王佳 . 低碳钢在海水中的阴极电化学行为[J]. 金属学报, 2010, 46(1): 123-128.
[13] 崔雷 杨善武 王树涛 高克玮 贺信莱. 锈层损伤对低碳贝氏体钢在含Cl-环境中腐蚀行为的影响[J]. 金属学报, 2009, 45(4): 442-449.
[14] 张红 齐慧滨 杜翠薇 李晓刚. 湿热环境中碱性泥浆附着下镀锌钢板的腐蚀行为[J]. 金属学报, 2009, 45(3): 338-344.
[15] 刘丽宏; 李; 明; 李晓刚; 卢燕平; 齐慧滨 . 耐候钢表面锈层稳定化处理用新型涂层研究[J]. 金属学报, 2004, 40(11): 1195-1199 .